For product technical information, pricing and availability contact our sales department at:
(219) 548-3799
[email protected]
BCN - Bonded Compression Neo
BCNF - Bonded Neo Ferrite Hybrid
BIF - Bonded Injection Ferrite
BIN - Bonded Injection Neo
BIS - Bonded Injection SmCo
N - Sintered NdFeB
C - Sintered SrFe2O3 Ferrites
S - Sintered SmCo5, Sm2Co17
A - Cast and Sintered AlNiCo
(219) 548-3799
[email protected]
BCN - Bonded Compression Neo
BCNF - Bonded Neo Ferrite Hybrid
BIF - Bonded Injection Ferrite
BIN - Bonded Injection Neo
BIS - Bonded Injection SmCo
N - Sintered NdFeB
C - Sintered SrFe2O3 Ferrites
S - Sintered SmCo5, Sm2Co17
A - Cast and Sintered AlNiCo
SmCo S-32
«« Back to Samarium Cobalt Magnetic Materials
| Max | Min |
| Residual Induction Br | G | 11,600 | 11,000 |
| Coercive Force Hc | Oe | 10,500 | 7,000 |
| Intrinsic Coercive Force Hci | Oe | 15,000 | 8,000 |
| Max. Energy Product (BH)max | MGOe | 33.0 | 30 |
| Material Density | g/cm3 | 8.4 | |
| Max. Operating Temperature | C | 250 | |
| Temperature Coefficient for B | %/C | -0.03 | |
| Temperature Coefficient for H | %/C | -0.04 | |
| Required Magnetizing Force | Oe | 35,000 | |
| Material Composition | Sm, Co, Cu, Zr, Pr | ||
Samarium Cobalt magnets have excellent temperature resistance to demagnetization and are used in high heat applications. Coating is not neccesary and tooling is not required.